Hastelloy X Nickel Based Superalloy - China

Hastelloy X(UNS NO6002) nickel-based superalloy Features and

applications overview: Hastelloy X is a nickel-based superalloy of

higher amount of iron.

The alloy uses chromium and molybdenum to conduct

solid solution strengthening.

It has good resistance to oxidation and

corrosion.

It has medium and lasting creep strength below 900°C.

It has

good formability and weldability in cold and hot processing.

This alloy

is suitable for the manufacture of aero-engine combustion chamber

components and other high temperature components.

It has a long-term

usage under 900°C.

Short-time working temperature reaches 1080°C.

Hastelloy X's similar grades: GH3536 GH536(China),

NC22FeD(France), NiCr22FeMo(Germany), Nimonic PE13(England)

Chemical composition, %

Nickel.

.

b alance Chromium.

.

20.5-


23.0 Iron.

.

1 7.0-20.0 Tungsten.

.

0.2-

1.0 Molybdenum.

.

8.0-10.0 Cobalt.

.

0 - 5-

2.5 Carbon.

.

0.05 -0.15

Manganese.

.

1.0 max

Silicon.

.

.

1.0 max

Sulfur.

.

.

0.015 max

Phosphorus.

.

0 - 025 max

Copper.

.

.

0.5 max

Aluminium.

.

0 - 15 max

Titanium.

.

.

0.5 max Physical

properties: Density, g/cm3 .

.

8.28

Melting Range, °C.

.

1295-1381 Thermal

conductivity, λ/(W/m•°C), at 100°C .

13.38 Specific heat,

J/kg•°C.

.

372.6 Elastic modulus,

GPa.

.

199 Electrical resistivity,

μΩ•m.

.

1.18 Coefficient of linear expansion,

a/10-6°C-1, at 20-100°C.

12 - 1 Mechanical properties: (the

minimum value detected at room temperature) Tensile strength,

σb/MPa.

.

690 Yield

strength, σp0.2/MPa.

.

275 Elongation, σ5

/%.

.

30 Brinell hardness,

HBS.

.

≥241 The way of heat treatment

is solution treatment

Available products and specifications:

Bar: ASTM B572, AMS 5754, ASME SB572

Forging: AMS 5754

Plate/Strip: ASTM B435, AMS 5536, ASME SB 435

Wire: AMS 5798

Pipe: ASTM B622, ASTM B619, ASTM B626, AMS 5587, ASME SB622, ASME SB619,

ASME SB626

The metallurgical structure of Hastelloy X :

The organization of the alloy in the solid solution is austenitic matrix, as well as a small amount of TiN and M6C type carbides.

The process performance and requirements of Hastelloy X:

1, The alloy has good cold and hot workability.

The forging heat temperature is 1170°C.

2, The average size of the grain size of the alloy is closely related to the forging deformation degree and the final forging temperature.

3, The alloy has a satisfactory weldability.

So for welding , argon arc welding, seam welding, spot welding and so on methods are all available.

4, The alloy may be added directly to the furnace whose operating temperature has been heated to the maximum point.

Released immediately after the necessary time in insulation, the alloy should be processed to the specifications.

If the metal temperature falls below the lowest processing temperature, the metal should be heated again.

3, The adhesion of the surface oxides of the alloy and the welding slags around the weld is stronger than that of stainless steel.

It is recommended to use fine grain abrasive belt and fine grain grinding wheel for polishing.

Hastelloy X Nickel Based Superalloy

For any questions and needs please contact us below

Company Contact:

• Posted By: Shanghai Kangsheng Superalloy Co., Ltd

• Phone: 8602169925078

• Address: 1355#,Chengbei road, Jiading District, Shanghai, Shanghai , China

• Email:

• Business Description: involved in international trade import export of goods, products, and services