Nimonic 93 Precipitation Hardening Nickel Based Alloy - China

Nimonic93 precipitation hardening nickel-based alloy Nimonic93's

features and applications overview: This alloy is a precipitation

hardened nickel based alloy containing higher amount of cobalt and

chromium.

It has high strength and good microstructural stability, and

has good overall performance below 850°C, This alloy is used for aero-

engine turbine blades, small engine turbine disk and fasteners.

Nimonic93's similar grades : GH93(China) Chemical composition, %:

Nickel.

.

b alance Chromium.

.

18.0-


21.0 Iron.

.

1 .

0 max

Boron.

.

0 .

02 max Cobalt.

.

15 - 0-

21.0 Carbon.

.

0.13 max

Manganese.

.

1.0 max

Silicon.

.

.

1.0 max

Sulfur.

.

.

0.015 max

Copper.

.

.

0.2 max Aluminium.

.

1.0-

2.0 Titanium.

.

2 - 0-3.0 Physical

properties Density, g/cm3 .

.

8.19

Melting Range, °C.

.

1360-1390 Thermal conductivity,

λ/(W/m•°C), at 100°C .

11.47 Specific heat,

J/kg•°C.

.

446 Elastic modulus, GPa.

226

Coefficient of linear expansion,

a/10-6°C-1, at 20-100°C.

11.91

Mechanical properties (the minimum value detected at room temperature)

Tensile strength, σb/MPa.

.

1080

Yield strength, σp0.2/MPa.

.

685

Elongation, σ5 /%.

.

20

Brinell hardness, HBS.

.

290

The way of heat treatment is solution treatment

The metallurgical structure of Nimonic93

The alloy precipitates the γ' phase on the austenitic matrix.

M23C6 -type carbides was chained on the grain boundaries.

MC-type carbides distribute within the grain in the granule-like forms, and no M7C3-type carbides are found.

The process performance and requirements of Nimonic93:

1, The plasticity of the alloy during hot working is good.

In the temperature of 1050-1150°C, it allows upsetting deformation of 80% but without cracking.

The forging cogging temperature is of 1130 to 1150°C, and the final forging temperature of not less than 950°C.

2, The average size of the grain size of the alloy is closely related to the forging deformation degree and the final forging temperature.

3, the plates can be welded using TIG joins.

In solution state, the weldability is still good.

After welding, it is a must to eliminate the stress and implement aging treatment.

4, The cutting performance of the alloy in the solid solution state is better than in the aging state.

Nimonic 93 Precipitation Hardening Nickel Based Alloy

Please see our contact information below

Company Contact:

• Posted By: Shanghai Kangsheng Superalloy Co., Ltd

• Phone: 8602169925078

• Address: 1355#,Chengbei road, Jiading District, Shanghai, Shanghai , China

• Email:

• Business Description: involved in international trade import export of goods, products, and services